Stain-resistant articles

ABSTRACT

The present invention relates to stain- or dye-resistant articles comprising a polymer composition (C) comprising: —at least one semi-aromatic polyamide comprising recurring units resulting from the condensation of terephthalic acid and at least one aliphatic diamine comprising more than 8 carbon atoms; —at least one filler; —from 0.1 to 35 wt. % of at least one white pigment, based on the total weight of the composition; wherein the color of said article has a lightness (L*) of at least 70 in the CIE 1976 (L*a*, b*) color space when measured according to ASTM E308-08.

REFERENCE TO RELATED APPLICATIONS

This application claims priority to U.S. application No. 61/392,856filed on 13 Oct. 2010, the whole content of this application beingincorporated herein by reference for all purposes.

FIELD OF THE INVENTION

The present invention broadly relates to low color articles comprising asemi-aromatic polyamide that feature surprisingly anti-stainingproperties. The present invention relates in particular to portableelectronic device housings comprising a polyamide composition featuringanti-staining properties. The invention relates also in particular tothe use of a semi-aromatic polyamide in the manufacture of articles forits anti-staining properties.

BACKGROUND OF THE INVENTION

Semi-aromatic polyamides (like those derived from phthalic acids andaliphatic diamines, i.e. polyphthalamides, or those derived fromaromatic diamines and aliphatic diacids) are polymers having excellentmechanical, physical and chemical properties which make them useful fora wide variety of different applications. Besides, they generallyfeature the benefit of being conveniently molded into a variety ofarticles of varying degrees of complexity and intricacy.

In particular, semi-aromatic polyamides are good candidates for themanufacture of articles such as portable electronic devices. Portableelectronic devices, such as mobile telephones, personal digitalassistants, laptop computers, tablet computers, global positioningsystem receivers, portable games, radios, cameras, camera accessories,and the like are becoming increasingly widely used globally in manydifferent environments. It is often important that the housings of suchdevices be made from materials that are able to withstand the rigors offrequent use and can meet challenging aesthetic demands while notinterfering with their intended operability. It is often desirable thatthose materials have good stiffness and high impact resistance, and thatthey exhibit high dimensional stability when they are formed (as byinjection molding, for example) into housings.

Many attempts have been made to offer a polyamide material suitable forthe manufacture of portable electronic devices housings. Most of themoffer a very good balance of properties useful in these specificapplications.

However, these prior art housings still suffer from a significantdrawback: they are not resistant to staining agents that are often putin contact with these portable electronic devices housings. Typicalstaining agents include: makeup (such as lipstick, lip gloss, lip liner,lip plumper, lip balm, foundation, powder, blush), artificial or naturalcolorants (such as those found in soft drinks, coffee, red wine,mustard, ketchup and tomato sauce), dyes and pigments (such as thosefound in dyed textiles and leather, used for the manufacture of portableelectronic devices housings). In contact with these staining agents, theprior art articles, and in particular the portable electronic deviceshousings are easily stained.

The staining issue of polyamides is known for a long time but in adifferent application, namely in the field of carpet and textile fibers.Polyamide fibers are relatively inexpensive and offer a desirablecombination of qualities such as durability, comfort, and ease ofmanufacture into a broad range of colors, patterns, and textures. As aresult, polyamide fibers are widely used in the home and industry ascarpets, drapery material, upholstery, and clothing. Carpets made frompolyamide fibers are a popular floor covering for residential andcommercial applications.

Polyamide fibers dye easily with dyes. Consequently, carpets made frompolyamide fibers stain easily when exposed to dyes or staining agentsthat exist in some common food and beverages. The resulting stainscannot be easily removed under ordinary cleaning conditions. The severestaining of carpeting is a major problem for consumers. In fact, surveysshow that more carpets are replaced because of staining than because ofwear.

Many attempts have been made to offer anti-staining polyamide carpetsand textiles that resist common household and common stains, therebyincreasing their life. For example, one way of avoiding such staining isto topically apply to the surface of the polyamide filaments materials aspecific anti-staining agent. U.S. Pat. No. 6,488,893 provides forexample a solution comprising condensation product of sulfonatednaphthalene sulphonic acid, and aldehyde and a dihydroxydiphenyl sulfonetogether with a methacrylic acid polymer that function as stain blockersso as to prevent stains from permanently coloring the yarn. Topicaltreatments, however, tend to be costly and non-permanent (washed awaywith one or more washings).

It would thus be desirable to obtain articles and in particular housingsfor portable electronic devices that are made from polyamidecompositions having excellent stiffness, high dimensional stability andimpact resistance while exhibiting also anti-staining properties.

It is thus a first object of the present invention to provideanti-staining polyamide articles. The polymer composition (C) accordingto the present invention exhibits outstanding properties: goodmechanical properties, high temperature resistance, low waterabsorption, superior chemical resistance. It can also be easilyprocessed and may be molded into thin walls. In addition, the inventorshave surprisingly found that the polymer composition (C) according tothe present invention features also outstanding anti-stainingproperties.

DETAILED DESCRIPTION OF THE INVENTION

In a first aspect, the present invention relates to a stain- ordye-resistant article comprising a polymer composition (C) comprising:

-   -   at least one semi-aromatic polyamide comprising recurring units        resulting from the condensation of terephthalic acid and at        least one aliphatic diamine comprising more than 8 carbon atoms;    -   at least one filler;    -   from 0.1 to 35 wt. % of at least one white pigment, based on the        total weight of the polymer composition (C);        wherein the color of said article has a lightness (L*) of at        least 70 in the CIE 1976 (L*, a*, b*) color space when measured        according to ASTM E308-08.

The present invention provides thus articles having excellentmechanical, physical and chemical properties while being alsosurprisingly stain- or dye-resistant.

In a second aspect, the present invention relates to a method forconferring anti-staining properties to an article comprising using asemi-aromatic polyamide comprising recurring units resulting from thecondensation of terephthalic acid and an aliphatic diamine comprisingmore than 8 carbon atoms.

The article according to the present invention exhibits outstandinganti-staining properties. More precisely, the article according to thepresent invention has a stain-resistance rating of 1 on the Stain RatingScale of the Stain Test Method described below. The staining is hereinintended to denote a coloration produced by a staining agent thatpenetrates a material. In many cases, stains can be affected by heat andmoisture, and may become reactive enough to bond with the underlyingmaterial. Extreme heat can cause a chemical reaction on an otherwiseremovable stain, turning it into a chemical compound that is impossibleto remove.

The staining agent is intended to denote any agent that causes thematerial that comes in contact with it to stain. Typically, stainingagents comprise at least one dye or pigment. Both dyes and pigmentsappear to be colored because they absorb and reflect some wavelengths oflight preferentially. Typical staining agents include: makeup (such aslipstick, lip gloss, lip liner, lip plumper, lip balm, foundation,powder, blush), artificial or natural colorants (such as those found insoft drinks, coffee, red wine, food), dyes and pigments (such as thosefound in dyed textiles and leather).

The Article

The article according to the present invention has a lightness (L*) ofat least 70 in the CIE 1976 (L*, a*, b*) color space when measuredaccording to ASTM E308-08. The procedure used to measure the color andin particular the luminance of the article is detailed here below:

The lightness (L*) was determined using a CE7000 Gretag MacBethspectrophotometer using Cool White Fluorescent (F2) illuminant, a 10°observer, a 10 nm wavelength interval, a spectral range of from 360 to700 nm and a D/8 optical geometry configuration with a bandpasscorrection using table 5.27 of the ASTM E 308-08 (on page 22). Valueswere measured on CIE Lab coordinates. The three coordinates of CIELABrepresent the lightness of the color (L*=0 yields black and L*=100indicates diffuse white; specular white may be higher), its positionbetween red and green (a*, negative values indicate green while positivevalues indicate red) and its position between yellow and blue (b*,negative values indicate blue and positive values indicate yellow).

The article according to the present invention has preferably alightness (L*) of at least 72, more preferably at least 74, still morepreferably at least 76, even more preferably of at least 78 and mostpreferably of at least 80.

The article according to the present invention may be composed of oneore more parts. At least one part of the article comprises the polymercomposition (C).

In a first particular embodiment, the article according to the presentinvention is an electronic equipment housing and more particularly aportable electronic device housing.

By “portable electronic device” is meant an electronic device that isdesigned to be conveniently transported and used in various locations.Representative examples of portable electronic devices include mobiletelephones, personal digital assistants, laptop computers, tabletcomputers, radios, cameras and camera accessories, watches, calculators,music players, global positioning system receivers, portable games, harddrives and other electronic storage devices, and the like.

By “portable electronic device housing” is meant a cover, backbone, orthe like of the device. The housing may be a single article or comprisetwo or more components. By “backbone” is meant a structural componentonto which other components of the device, such as electronics,microprocessors, screens, keyboards and keypads, antennas, batterysockets, and the like are mounted. The backbone may be an interiorcomponent that is not visible or only partially visible from theexterior of the telephone. The housing may provide protection forinternal components of the device from impact and contamination and/ordamage from environmental agents (such as liquids, dust, and the like).Housing components such as covers may also provide substantial orprimary structural support for and protection against impact of certaincomponents having exposure to the exterior of the device such as screensand/or antennas. Examples of such housings include but are not limitedto: mobile telephones housings, personal digital assistants housings,laptop computers housings, tablet computers housings, global positioningsystem receivers housings, portable games housings, radios housings,cameras housings, camera accessories housings, etc.

In a preferred embodiment, the housings of the present invention aremobile telephone housings. By “mobile telephone housing” is meant one ormore of the back cover, front cover, antenna housing, and/or backbone ofa mobile phone. The housing may be a single article incorporating one ormore of the foregoing. By “backbone” is meant a structural componentonto which other components of the mobile telephone, such aselectronics, screens, battery sockets, and the like are mounted. Thebackbone may be an interior component that is not visible or onlypartially visible from the exterior of the telephone.

The articles and in particular the housings for portable electronicdevices according to the present invention are made from thecompositions using any suitable melt-processing method. In particular,the article according to the present invention may be an injectionmolded article, an extruded molded article, a shaped article, a coatedarticle or a casted article. Injection molding is a preferred method.

In a second particular embodiment, the article according to the presentinvention is selected from:

-   -   an appliance like a http://en.wikipedia.org/wiki/Home_appliance        home appliance or household machines such as refrigerators,        freezers, blenders, can openers, coffee machines, microwave        ovens, convection ovens, mixers, stoves, washing machines,        dishwashers, trash compactors and the like;    -   a countertop referring to a horizontal worksurface in kitchens        or other food preparation areas, bathrooms or lavatories, and        workrooms in general;    -   furnitures like cabinets, chairs, tables and the like.

The Semi-Aromatic Polyamide

The semi-aromatic polyamide according to the present invention comprisesrecurring units (R) resulting from the condensation of terephthalic acidand at least one aliphatic diamine comprising more than 8 carbon atoms.

Recurring units (R) are advantageously obtained from the condensation ofterephthalic acid and at least one aliphatic diamine comprising morethan 8 carbon atoms. Preferably, they are obtained from the condensationof terephthalic acid and at least one aliphatic diamine comprising lessthan 14 carbon atoms, more preferably less than 13 carbon atoms, evenmore preferably less than 12 carbon atoms. Excellent results wereobtained when using one or more aliphatic diamine comprising 9, 10 or 11carbon atoms.

Suitable aliphatic diamine comprising more than 8 carbon atoms include,but are not limited to, 1,8-octanediamine, 1,9-nonanediamine,2-methyl-1,8-octanediamine, 1,10-decanediamine, 1,12-dodecanediamine,2,2,4-trimethyl-1,6-hexanediamine, 2,4,4-trimethyl-1,6-hexanediamine and5-methyl-1,9-nonanediamine; it may also be an alicyclic diamine, e.g.methylcyclohexanediamine and isophoronediamine.

The aliphatic diamine having more than 8 carbon atoms is preferably aC₉-C₁₄ diamine, more preferably a C₉-C₁₂ diamine.

In a particular embodiment, the aliphatic diamine having more than 8carbon atoms is a C9 diamine. In such a case, the diamine may be1,9-nonanediamine (NDA) and/or 2-methyl-1,8-octanediamine (MODA). The2-methyl-1,8-octanediamine (MODA) may be present from 0 to 50 mole %,based on the total number of moles of the diamine. When the aliphaticdiamine having more than 8 carbon atoms is a mix of NDA and MODA, themolar ratio [(NDA): (MODA)] is advantageously of at least 1, preferablyof at least 2, more preferably of at least 3 and still more preferablyof at least 4; besides, it is advantageously of at most 9, preferably ofat most 7, and more preferably of at most 6.

Excellent results were obtained when the invented polyamide consistedessentially of:

-   -   a diamine component (a) consisting essentially of a mixture of        1,9-nonanediamine and 2-methyl-1,8-octanediamine in a molar        ratio [(NDA): (MODA)] of about 1.5 or 5.6, and    -   a dicarboxylic acid component (b) consisting essentially of        terephthalic acid.

Preferred polyamides are those often referred to as PA 9T, PA 10T and PA11T and mixtures thereof.

PA 9T, when made using 1,9-nonanediamine, is a polyamide the recurringunits of which have the following structure:

PA 10T is a polyamide the recurring units of which have the followingstructure:

PA 10T may be prepared by various ways. It is advantageously prepared atleast partially from decanediamine derived from a renewable raw materialsuch as castor bean.

PA 11T is a polyamide the recurring units of which have the followingstructure:

The semi-aromatic polyamide according to the present invention maycomprise other recurring units than recurring units (R).

The semi-aromatic polyamide according to the present invention may beobtained by the condensation of one or more dicarboxylic acids and oneor more diamines, and/or one or more aminocarboxylic acids, and/orring-opening polymerization products of one or more cyclic lactams.

In addition to terephthalic acid (abbreviated as “T” in polyamidedesignations), suitable dicarboxylic acids include, but are not limitedto, succinic acid, glutaric acid, sebacic acid, adipic acid, azelaicacid, 1,6-cyclohexanedicarboxylic acid, naphthalenedicarboxylic acid andisophthalic acid (abbreviated as “I” in polyamide designations).Preferably, adipic acid is present in an amount of at most 30 mol %,more preferably at most 20 mol %, even more preferably at most 10 mol %,based on the total number of moles of the diacid component. Mostpreferably the diacid component is free of adipic acid.

Suitable diamines include, but are not limited to,tetramethylenediamine, hexamethylenediamine, octamethylenediamine,nonamethylenediamine, decamethylenediamine, dodecamethylenediamine,2-methylpentamethylenediamine, 2-methyloctamethylenediamine,trimethylhexamethylenediamine, bis(p-aminocyclohexyl)methane,m-xylylenediamine, and p-xylylenediamine.

In a particular embodiment, another aliphatic diamine is used inaddition to the aliphatic diamine comprising more than 8 carbon atoms.This additional aliphatic diamine may comprise from 6, 7, 8, 9 or 10carbon atoms. Excellent results were obtained with PA 6T/10T.

The semi-aromatic polyamide according to the present invention comprisespreferably at least 20 wt. %, more preferably at least 40 wt. %, evenmore preferably at least 50 wt. %, still more preferably at least 60 wt.% and most preferably at least 80 wt. % of recurring units (R) based onthe total weight of the semi-aromatic polyamide. Excellent results wereobtained when the semi-aromatic polyamide was essentially free or evencompletely free of recurring units other than recurring units (R).

More than one semi-aromatic polyamide may be present in the polymercomposition (C). In such a case, the semi-aromatic polyamide comprisingrecurring units resulting from the condensation of terephthalic acid andat least one aliphatic diamine comprising more than 8 carbon atomsdetailed above is present in at least 20 wt. %, more preferably at least40 wt. %, even more preferably at least 50 wt. %, still more preferablyat least 60 wt. % and most preferably at least 70 wt. %, based on thetotal weight of the semi-aromatic polyamides.

The semi-aromatic polyamide according to the present invention hasadvantageously a high melting point. Its melting point is preferablyabove 200° C., more preferably above 240° C., even more preferably above280° C. and most preferably above 300° C. Excellent results wereobtained with a semi-aromatic polyamide featuring a melting point of316° C.

The semi-aromatic polyamide according to the present invention hasadvantageously a high heat deflection temperature. Its heat deflectiontemperature is preferably above 200° C., more preferably above 250° C.,even more preferably above 270° C. and most preferably above 290° C.Excellent results were obtained with a semi-aromatic polyamide featuringa heat deflection temperature of 295° C.

The semi-aromatic polyamide according to the present invention havingadvantageously a high heat deflection temperature and a high meltingpoint, it features therefore excellent high temperature resistance.

The semi-aromatic polyamide according to the present invention ispreferably present in the polymer composition (C) in an amount of atleast 10 wt. %, more preferably of at least 20 wt. %, still morepreferably of at least 30 wt. % and most preferably of at least 40 wt.%, based on the total weight of the polymer composition (C). On theother hand, the semi-aromatic polyamide according to the presentinvention is preferably present in the polymer composition (C) in anamount of at most 90 wt. %, more preferably of at most 80 wt. %, stillmore preferably of at most 70 wt. % and most preferably of at most 60wt. %, based on the total weight of the polymer composition (C).Excellent results were obtained when the semi-aromatic polyamideaccording to the present invention was present in the polymercomposition (C) in about 50 wt. %, based on the total weight of thepolymer composition (C).

The Filler

The polymer composition (C) further comprises at least one filler. Thefiller may be selected from the group consisting of fibrous fillers,particulate fillers and mixture thereof.

Examples of such filler include, but are not limited to, glass fiber,carbon fiber, glass fibers having a non-circular cross section, glassflakes, carbon fibers, wollastonite, calcined clay, kaolin, and thelike.

In a particular embodiment of the present invention, the filler ispreferably a particulate filler. Examples of such particulate fillerinclude carbon black, talc, glass balls, calcium silicate, calciummetasilicate, kaolin, chalk, powdered quartz, alumina, boron nitride,mica, aluminium silicate, calcium carbonate, clay and the like.

In another particular embodiment of the present invention, the filler ispreferably a fibrous filler.

The fibrous filler may have a circular or a non-circular cross sectionhaving a major axis lying perpendicular to a longitudinal direction ofthe reinforcing agent and corresponding to the longest linear distancein the cross section. The non-circular cross section has a minor axiscorresponding to the longest linear distance in the cross section in adirection perpendicular to the major axis. The ratio of the length ofthe major axis to that of the minor access is preferably between about1.5:1 and about 6:1. The ratio is more preferably between about 2:1 and5:1 and yet more preferably between about 3:1 to about 4:1.

The fibrous reinforcing agent may be glass, carbon fibers, ceramicfibers or other materials. Glass fibers are preferred. The fibrousreinforcing agent may be in the form of long glass fibers, choppedstrands, milled short glass fibers, or other suitable forms known tothose skilled in the art. Particularly preferred according to theinvention are glass fibers having a fiber diameter between 7 and 18 μm,preferably between 9 and 15 p.m.

In a further particular embodiment of the present invention, the filleris preferably a mixture of particulate and fibrous filler.

In a preferred embodiment, the polymer composition (C) comprisespreferably at least 20 wt. %, more preferably at least 30 wt. %, stillmore preferably at least 40 wt. % and most preferably at least 45 wt. %of the filler, based on the total weight of the polymer composition (C).On the other hand, the polymer composition (C) comprises preferably atmost 80 wt. %, more preferably at most 70 wt. %, still more preferablyat most 60 wt. % and most preferably at most 55 wt. % of the filler,based on the total weight of the polymer composition (C).

The Pigment

The polymer composition (C) further comprises from 0.1 to 35 wt. % of atleast one white pigment, based on the total weight of the polymercomposition (C), different from the above described filler.

Among white pigments, the white pigment according to the presentinvention is preferably selected from titanium dioxide, barium sulfate,zinc sulfide and mixtures thereof. More preferably, the white pigment istitanium dioxide or zinc sulfide.

The polymer composition (C) comprises advantageously from 0.1 to 35 wt.%, preferably from 1 to 20 wt. %, more preferably from 2 to 10 wt. % andstill more preferably from 3 to 8 wt. % of at least one white pigmentbased on the total weight of the composition.

In addition to the at least one white pigment, the polymer composition(C) may comprise other inorganic and organic pigments. Such pigments arewell known from the skilled person and are notably chosen from: ironoxide pigments, chromium oxide green, lead chromate molybdate pigments,cadmium pigments, mixed metal oxide pigments, ultramarine blue, etc.

The total amount of pigments (taking into account both white pigmentsand other pigments) according to the present invention are preferablypresent in the composition (C) in an amount of at least 0.1 wt. %, morepreferably of at least about 0.5 wt. %, yet more preferably of at leastabout 3 wt. %, or still more preferably of at least about 4 wt. %, basedon the total weight of the polymer composition (C). On the other hand,the pigments according to the present invention are preferably presentin the polymer composition (C) in an amount of at most 35 wt. %, morepreferably of at most 25 wt. %, yet more preferably of at most 15 wt. %,or still more preferably of at most 10 wt. %, and most preferably of atmost 8 wt. %, based on the total weight of the composition. Excellentresults were obtained when the pigments were present in the polymercomposition (C) in about 5 wt. %, based on the total weight of thepolymer composition (C).

Optional Ingredients

The polymer composition (C) may further comprise other ingredients. Forexample, the polymer composition (C) may further comprise otherpolymer(s). In particular, the polymer composition (C) may furthercomprise other polyamides including aliphatic polyamides such aspolyamide 6; polyamide 6,6; polyamide 4,6; polyamide 6,10; polyamide6,12; polyamide 11; polyamide 12; polyamide 9,10; polyamide 9,12;polyamide 9,13; polyamide 9,14; polyamide 9,15; polyamide 6,16;polyamide 9,36; polyamide 10,10; polyamide 10,12; polyamide 10,13;polyamide 10,14; polyamide 12,10; polyamide 12,12; polyamide 12,13;polyamide 12,14; polyamide 6,14; polyamide 6,13; polyamide 6,15;polyamide 6,16; polyamide 6,13; and semi-aromatic polyamides such aspoly(m-xylylene adipamide) (polyamide MXD,6), poly(dodecamethyleneterephthalamide) (polyamide 12,T), poly(nonamethylene terephthalamide)(polyamide 9,T), hexamethylene adipamide/hexamethylene terephthalamidecopolyamide (polyamide 6,T/6,6), hexamethylene terephthalamide.

The polymer composition (C) may optionally further comprise an impactmodifier. Preferred impact modifiers include those typically used forpolyamides, including carboxyl-substituted polyolefins, which arepolyolefins that have carboxylic moieties attached thereto, either onthe polyolefin backbone itself or on side chains. By “carboxylicmoieties” is meant carboxylic groups such as one or more of dicarboxylicacids, diesters, dicarboxylic monoesters, acid anhydrides, andmonocarboxylic acids and esters. Useful impact modifiers includedicarboxyl-substituted polyolefins, which are polyolefins that havedicarboxylic moieties attached thereto, either on the polyolefinbackbone itself or on side chains. By dicarboxylic moiety′ is meantdicarboxylic groups such as one or more of dicarboxylic acids, diesters,dicarboxylic monoesters, and acid anhydrides.

The impact modifier may preferably be based on anethylene/.alpha.-olefin polyolefin. Diene monomers such as1,4-butadiene; 1,4-hexadiene; or dicyclopentadiene may optionally beused in the preparation of the polyolefin. Preferred polyolefins includeethylene-propylene-diene (EPDM) polymers made from 1,4-hexadiene and/ordicyclopentadiene and styrene-ethylene-butadiene-styrene (SEBS)polymers. As will be understood by those skilled in the art, the impactmodifier may or may not have one or more carboxyl moieties attachedthereto.

The carboxyl moiety may be introduced during the preparation of thepolyolefin by copolymerizing with an unsaturated carboxyl-containingmonomer. Preferred is a copolymer of ethylene and maleic anhydridemonoethyl ester. The carboxyl moiety may also be introduced by graftingthe polyolefin with an unsaturated compound containing a carboxylmoiety, such as an acid, ester, diacid, diester, acid ester, oranhydride. A preferred grafting agent is maleic anhydride. A preferredimpact modifier is an EPDM polymer grafted with maleic anhydride, suchas Royaltuf 498, which is commercially available from Chemtura. Blendsof polyolefins, such as polyethylene, polypropylene, and EPDM polymerswith polyolefins that have been grafted with an unsaturated compoundcontaining a carboxyl moiety may be used as an impact modifier.

Impact modifier is present in the composition in 0 to about 20 weightpercent, or preferably in about 3 to about 20 weight percent, or morepreferably in about 5 to about 15 weight percent, based on the totalweight of the composition.

The polymer composition (C) may further optionally comprise additionaladditives such as ultraviolet light stabilizers, heat stabilizers,antioxidants, processing aids, lubricants, flame retardants, and/orconductivity additive such as carbon black and carbon nanofibrils.

In a preferred embodiment, the polymer composition (C) comprises:

-   -   preferably at least 30 wt. % and more preferably at least 40 wt.        % of the at least one semi-aromatic polyamide comprising        recurring units resulting from the condensation of terephthalic        acid and at least one aliphatic diamine comprising more than 8        carbon atoms;    -   preferably at least 20 wt. %, more preferably at least 30 wt. %,        of the at least one filler;        -   from 0.1 to 35 wt. % and preferably from 2 to 10 wt. % of at            least one white pigment, based on the total weight of the            polymer composition (C).

A further embodiment of the present invention relates to a method forconferring anti-staining properties to an article comprising using asemi-aromatic polyamide comprising recurring units resulting from thecondensation of terephthalic acid and an aliphatic diamine comprisingmore than 8 carbon atoms for the manufacture of said article. Sucharticle may be an injection molded article, an extruded molded article,a shaped article, a coated article or a casted article. For example,such article may be selected from the group consisting of mobiletelephone housings, personal digital assistants housings, laptopcomputers housings, tablet computer housings, global positioning systemreceiver housings, portable game housings, radio housings, camerashousings or camera accessory housings.

The semi-aromatic polyamide preferably used in the manufacture ofarticles for its anti-staining properties may be PA 9T, PA 10T, PA 11Tor mixtures thereof.

In particular, the present invention relates to a method for conferringanti-staining properties to an article comprising using a compositioncomprising PA 9T, PA 10T, PA 11T or mixtures thereof for the manufactureof said article. The Applicant has surprisingly found out that the useof such compositions in the manufacture of articles reduce dramaticallytheir staining when exposed to external staining agents.

Should the disclosure of any patents, patent applications, andpublications which are incorporated herein by reference conflict withthe description of the present application to the extent that it mayrender a term unclear, the present description shall take precedence.

Examples

Makeup was used as the staining agent. More precisely, the makeup wasMaybelline Blush 10 Romantic Plum blush.

This staining agent was tested on various 0.3 cm thick molded plaquesmade of different materials:

PA 6,6: Zytel® 101 commercialized by E. I. du Pont de Nemours andCompanyPA 6T/6,6: AMODEL® A-4122 L WH905 commercialized by SOLVAY ADVANCEDPOLYMERS, L.L.C.PA6T/61/6,6: AMODEL® A-1133 NL WH505 commercialized by SOLVAY ADVANCEDPOLYMERS, L.L.C.PA 10,10: Commercially available from Shandong Dongchen EngineeringPlastic Co., Ltd.PA 10,12: Commercially available from Shandong Dongchen EngineeringPlastic Co., Ltd.PA 9T: polymer obtained by the condensation of C9 aliphatic diamine andterephthalic acid, supplied by Kuraray.PA 10T: Vicnyl 700 commercialized by Kingfa.Glass fiber: CSG3PA-820 commercialized by Nitobo.Colored pigments: a mixture of pigments were used for color matching.White pigment I: zinc sulfide: Sachtolith® HD-L commercialized bySachtleben Chemie GmbH.White pigment II: titanium dioxide: R-105 commercialized by DuPontTitanium Technologies.Talc: Steamic® OOS commercialized by Talc de Luzenac France.Sebum: Synthetic sebum commercialized by Scientific Services.

TABLE 1 Materials tested CE1 CE2 CE3 CE4 CE5 E1 E2 Polyamide PA 6,6 50PA 6T/6,6 66 PA 6T/6I/6,6 58.7 PA 10,10 46.22 PA 10,12 46.22 PA 9T 46.22PA 10T 46.22 Filler Glass fiber 50 21 34.5 47.26 47.26 47.26 47.26Pigments Colored pigments 0.025 0.025 0.025 0.025 White pigment I 4.7554.755 4.755 4.755 White pigment II 12 6 Additives Typical PA additives 10.5 0.74 0.74 0.74 0.74 Talc 0.3 1 1 1 1

Staining Test Method

The color of the plaques were measured, and in particular the lightness(L*) of the samples were determined using a CE7000 Gretag MacBethspectrophotometer using Cool White Fluorescent (F2) illuminant and the10° observer, as detailed above.

The following test procedure was used to determine the stain-resistanceperformance of examples of this invention, this test method simulates apotential real life method of staining whereby a person wearing makeuptalking on their cell phone may introduce colorants to the plastic cellphone part. Synthetic face oil, sebum, was used to simulate a possiblecarrier or solvent for the dyes.

A mixture of staining agent is prepared by heating sebum until it isliquid, then mixing 3 parts of the heated sebum to one part of themakeup and finally heating the mixture to maintain liquidity.

The prepared staining agent mixture is applied to the surface of themolded plaques with a cotton swab. The plaques are placed in anenvironmental chamber at 65° C. and 90% humidity for 24 hours. Themolded plaques are then placed at room temperature before wiping theirsurface with isopropyl alcohol. Once cleaned, the plaques are finallyinspected for staining.

The inspection step comprises the measurement of the lightness (L*), asdetailed above. The difference between the original L* measured and theL* measured after the staining treatment is calculated.

Stain Rating Scale: the stains can be categorized according to thefollowing standards:

1=no staining=Δ L≦0.52=moderate staining=0.5<Δ L<53=heavy staining=Δ L>5

In other words, a stain-rating of 1 is excellent, showing good stainresistance, whereas 3 is a poor rating, showing persistence of heavystaining. For a substrate to be considered to have adequate stainresistance, it should have a rating of 1 on the above-described StainRating Scale.

TABLE 2 Staining test results CE1 CE2 CE3 CE4 CE5 E1 E2 Initial L* value61.6 91.0 93.9 90.9 90.8 89.7 89.4 L* value after staining 58.4 90.092.7 84.3 84 89.7 89.0 treatment Staining rating 2 2 2 3 3 1 1

1-15: (canceled)
 16. An article comprising a polymer composition (C)comprising: at least one semi-aromatic polyamide comprising recurringunits resulting from the condensation of terephthalic acid and at leastone aliphatic diamine comprising 9 to 12 carbon atoms; from 30 to 80 wt.% of at least one filler; and from 0.1 to 35 wt. % of at least one whitepigment, based on the total weight of the polymer composition (C);wherein the color of said article has a lightness (L*) of at least 70 inthe CIE 1976 (L*, a*, b*) color space when measured according to ASTME308-08 and the article is selected from the group consisting of amobile telephone housing, a personal digital assistants housing, alaptop computers housing, a tablet computer housing, a globalpositioning system receiver housing, a portable game housing, a radiohousing, a camera housing and a camera accessory housing.
 17. Thearticle according to claim 16, wherein the semi-aromatic polyamide isselected from the group consisting of PA9T, PA10T, PA11T, PA12T andmixtures thereof.
 18. The article according to claim 16, wherein the atleast one aliphatic diamine comprises 1,9-nonanediamine; 2methyl-1,8-octanediamine; 1,110-decanediamine or a combination thereof.19. The article according to claim 16, wherein the polymer composition(C) comprises at least 40 wt. % of the semi-aromatic polyamide, based onthe total weight of the polymer composition (C).
 20. The articleaccording to claim 16, wherein the polymer composition (C) comprises atleast 40 wt. % to 80 wt. % of the at least one filler, based on thetotal weight of the polymer composition (C).
 21. The article accordingto claim 16, wherein the polymer composition (C) comprises at least 1wt. % to 35 wt. % of the at least one white pigment, based on the totalweight of the polymer composition (C).
 22. The article according toclaim 16, wherein the at least one filler is glass fiber orwollastonite.
 23. The article according to claim 16, wherein the whitepigment is selected from the group consisting of titanium dioxide,barium sulfate and zinc sulfide.
 24. The article according to claim 16,wherein the white pigment comprises zinc sulfide.
 25. The articleaccording to claim 16, wherein the article is selected from the groupconsisting of a mobile telephone housing, a personal digital assistantshousing, a laptop computers housing, and a tablet computer housing. 26.The article according to claim 16, wherein the article is selected fromthe group consisting of a mobile telephone housing, a laptop computerhousing, and a tablet computer housing.
 27. The article according toclaim 16, wherein the article is an injection molded article, anextruded molded article, a shaped article, a coated article or a castedarticle.
 28. The article according to claim 16, wherein the articlecomprises a stain-resistance rating of 1 on the Stain Rating Scale ofthe Stain Test Method.
 29. A method for conferring anti-stainingproperties to an article, the method comprising forming at least aportion of the article of claim 16 from the semi-aromatic the polymercomposition (C).
 30. The method according to claim 29, wherein theforming comprises injection molding, extrusion molding, a shaping,coating or casting the article from the polymer composition (C).